Effect of the electrode layer on the polydomain structure of epitaxial PbZr0.2Ti0.8O3 thin films

Journal Article

Alpay, S.P., V. Nagarajan, L.A. Bendersky, M.D. Vaudin, S. Aggarwal, Ramamoorthy Ramesh, A.L. Roytburd

10.1063/1.369670

PbZr0.2Ti0.8O3(PZT) thin films with and without La0.5Sr0.5CoO3(LSCO) electrodes were grown epitaxially on (001) SrTiO3 at 650°C by pulsed laser deposition. The domain structure of the 400 nm thick PZT films with different electrode layer configurations was investigated by x-ray diffraction and transmission electron microscopy. The c-domain fractions of the PZT films with no electrode layer, with a 50 nm electrode layer between the film and the substrate, and with 50 nm electrode layers on top and bottom of the PZT film were found to be equal. Theoretical estimation of the c-domain fraction based on the minimization of the energy of internal stresses in films is in good agreement with experimental results. This means that depolarizing fields do not affect the polydomain structure of the film. Calculations of the in-plane strains based on the lattice parameters of the LSCO layer in the above configurations led to the conclusion that the bottom electrode layer is coherently strained to match the substrate. © 1999 American Institute of Physics.

Journal of Applied Physics

85

1999

00218979

cited By 83

Ramesh Lab